Moisture curing polyurethane hot melt adhesive, the adhesion and toughness can be adjusted, with excellent bonding strength, temperature resistance, chemical corrosion resistance.
Mainly applied for smart phones, tablet, smart watch TP and frame bonding, wearable devices such as bracelet and VR devices, control panel bonding of home appliances, vehicle lighting, FPC fixed bonding.
Product Model | Color | Viscosity (cps 100℃) |
Open Time | Lap Shear Strength | More Parameters |
---|---|---|---|---|---|
AP9101 | Creamy white | 4000~6000 | 2~4min 25℃ | 10~12MPa (PC/PC) |
Detailed introduction |
AP9102 | Transparent / Black | 2000~3000 | 2~4min | 7~9MPa (PC/PC) |
Detailed introduction |
AP9108 | Yellowish transparent / Black | 4000~6000 | 2~4min | 8~10MPa (PC/PC) |
Detailed introduction |
AP9109 | Translucent / Black | 9000~12000 | 2~4min | 8~10MPa (PC/PC) |
Detailed introduction |
AP9110 | Yellowish transparent / Black | 5000~7000 | 3~5min | 7~8MPa (PC/PC) |
Detailed introduction |
AP9112 | Yellowish transparent / Black | 5000~7000 | 3~5min | 10~12MPa (PC/PC) |
Detailed introduction |
AP9131 | Creamy white / Black / Silver | 5000~7000 | 2~4min 25℃ | 9~11MPa (PC/PC) |
Detailed introduction |
AP9133 | Creamy white / Black | 7000~9000 | 2~3min 25℃ | 12~15MPa (PC/PC) |
Detailed introduction |
AP9135 | Light yellow transparent | 5000~7000 | 3~5min 25℃ | ≥10MPa (PC/PC) |
Detailed introduction |
AP9161 | Creamy white / Black | 5000~7000 | 3~5min 25℃ | 10~12MPa (PC/PC) |
Detailed introduction |
AP9166 | Creamy white / Black | 5000~7000 | 3~5min 25℃ | 11~13MPa (PC/PC) |
Detailed introduction |
AP9201 | Transparent / Black | 5000~7000 | 2~4min 25℃ | 8~10MPa | Detailed introduction |
AP9210 | Yellowish transparent / Black / Silver gray | 5000~7000 | 3~5min | 8~10MPa (PC/PC) |
Detailed introduction |
AP9406 | Black | 4000~6000 | 3~5min 25℃ | 9~11MPa | Detailed introduction |
AP9408 | Transparent / Black | 7000~10000 | 2~3min 25℃ | 8~10MPa | Detailed introduction |
AP9415 | Black | 5000~7000 | 3~5min 25℃ | 10~12MPa | Detailed introduction |